Gasifier Vessel Fitness for Service
CLIENT |
Energy Holding Company |
LOCATION |
Indiana |
Fitness for Service Assessment for Reformer Top Nozzle
The upper part of this vessel was found to be susceptible to dew point corrosion. In this phenomenon, the shell becomes cold enough in localized areas to cause process fluids to condense on the wall, leading to localized corrosion in these lower temperature sections. The specific area of concern was the top head near the inlet nozzle, where corrosion had progressed substantially since the vessel was placed in service. WJE was engaged to perform analysis and a Fitness for Service (FFS) assessment of the flange head.
BACKGROUND
The top head of a high-temperature reformer was suffering dew point corrosion under the refractory meant to protect the low alloy steel shell from the intense heat of the process.
SOLUTION
For FFS assessments, advanced computer analyses are often employed to analyze nonuniform loads or material configurations. The assessment of the reformer head employed the ABAQUS FEA suite to evaluate the combined impact of bolt loads, gasket interactions, component contact, and nonuniform thinning based on inspections conducted by the plant’s team.
Material models were used to mimic different minimum tensile strengths. Internal pressure was applied to all internal metal surfaces and bolt pretension was added. The models demonstrated that the corroded region was fit for service at the time of evaluation, but corrosion at the historical rate could result in the vessel falling below the assessment limit in less than two years from the time of reporting. WJE recommended that the plant explore options to repair, remediate, or replace the damaged components, and to plan for future surveillance of the area.
RELATED INFORMATION
-
Our metallurgical and applied mechanics engineers provide solutions related to design... MORE >Services | Metallurgy and Applied Mechanics
-
WJE fracture mechanics consultants have provided fracture mechanics assessment and fitness for... MORE >Services | Fracture Mechanics Assessment and Fitness for Service
-
WJE's primary goal of performing a metallurgical failure analysis is to determine the root cause... MORE >Services | Metallurgical Failure Analysis
-
API 579-1 Fitness for Service Assessment of Local Thinning MORE >Projects | Flare Knockout Drum